Fischer-Tropsch Process, Supported Fischer-Tropsch Synthesis Catalyst and Uses Thereof

ABSTRACT

A process for converting a mixture of hydrogen and carbon monoxide gases to a composition comprising alcohols and liquid hydrocarbons by means of a Fischer-Tropsch synthesis reaction, said process comprising contacting a mixture of hydrogen and carbon monoxide gases, preferably in the form of synthesis gas mixture, with a supported Co—Mn Fischer-Tropsch synthesis catalyst, wherein: the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria; the supported synthesis catalyst comprises at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; the weight ratio of manganese to cobalt, on an elemental basis, is 0.2 or greater; the molar ratio of hydrogen to carbon monoxide is at least 1; and, the Fischer-Tropsch synthesis reaction is conducted at a pressure in the range of from 1.0 to 10.0 MPa absolute.

This invention relates to a Fischer-Tropsch process employing a supported Fischer-Tropsch s synthesis catalyst containing both cobalt and manganese, as well as the synthesis catalyst itself and a method for its preparation. Also provided is the use of a supported Co—Mn Fischer-Tropsch synthesis catalyst for increasing the selectivity of a Fischer-Tropsch process for the production of alcohols and/or liquid hydrocarbons, and/or for increasing conversion in a Fischer-Tropsch process.

The conversion of synthesis gas into hydrocarbons by the Fischer-Tropsch process has been known for many years. The growing importance of alternative energy sources has seen renewed interest in the Fischer-Tropsch process as one of the more attractive direct and environmentally acceptable routes to high quality transportation fuels and lubricants.

Many metals, for example cobalt, nickel, iron, molybdenum, tungsten, thorium, ruthenium, rhenium and platinum are known to be catalytically active, either alone or in combination, in the conversion of synthesis gas into hydrocarbons and oxygenated derivatives thereof. Of the aforesaid metals, cobalt, nickel and iron have been studied most extensively. Generally, the metals are used in combination with a support material, of which the most common are alumina, silica and carbon. In the preparation of supported cobalt-containing Fischer-Tropsch synthesis catalysts, a solid support material is typically impregnated with a cobalt-containing compound, which may for instance be an organometallic or inorganic compound (e.g. Co(NO₃)₂.6H₂O), by contacting with a solution of the compound. The particular form of cobalt-containing compound is generally selected for its ability to form a cobalt oxide (for instance, CoO, Co₂O₃ or Co₃O₄) following a subsequent calcination/oxidation step. Following generation of the supported cobalt oxide, a reduction step is necessary in order to form the pure cobalt metal as the active catalytic species. Thus, the reduction step is also commonly referred to as an activation step.

During calcination, cobalt oxides form crystallites on the support material, and the properties of such crystallites, such as dispersion, particle size and reduction degree, are known to have an effect on the activity and selectivity of the catalyst in Fischer-Tropsch processes. For example, de Jong et al. (J. Am. Chem. Soc., 128, 2006, 3956-3964) showed that for optimal activity and selectivity for C5₊ hydrocarbons, cobalt metal particles in the active catalyst having sizes of around 6 to 8 nm are particularly beneficial.

Typically, the principal focus in adapting Fischer-Tropsch synthesis catalysts is for improving activity and selectivity for C5+ hydrocarbons (paraffins). Nevertheless, alcohols and liquid hydrocarbons are also desirable products of the Fisher-Tropsch process and process conditions and synthesis catalyst design may be tailored to favour the production of those materials.

Hydrocarbon fuel deriving from Fischer-Tropsch processes are better able to meet increasingly stringent environmental regulations, as compared with conventional refinery fuel, since hydrocarbon fuel obtainable from the Fischer-Tropsch process is essentially free of sulfur and aromatic compounds and has a low nitrogen content. This may result in much lower emissions of pollutants such as CO, CO₂, SO₂, and NO_(R), as well as little or no particulate emissions. Meanwhile, alcohols deriving from Fischer-Tropsch processes have a higher octane rating than hydrocarbons and thus can burn more completely, thereby reducing the environmental impact of such a fuel. Alcohols obtained from a Fischer-Tropsch reaction may also be advantageously used as reagents in other processes, such as polymerisation, surfactants, and cosmetics, a particular benefit being the purity of the alcohols obtainable by a Fischer-Tropsch process. Long-chained alcohols are also particularly useful as lubricant components, or precursors thereof. Linear alpha olefins (LAO) and linear alcohols have significant value as a basis for fine chemicals, lubricants and plasticisers/polymers.

de Jong et al. discussed above does not focus on the impact of cobalt particle size on the activity and selectivity for producing alcohols or liquid hydrocarbons. FIG. 9 of de Jong et al. indicates that methane selectivity is higher where the cobalt particle size is less than 5 nm and that selectivity for methane remains relatively constant for increases in cobalt particle size above 5 nm for the Fischer-Tropsch process conditions tested.

It would be desirable to provide a means for improving the activity and selectivity of a Fischer-Tropsch process for the production of alcohols and liquid hydrocarbons, in particularly alcohols and olefins, and especially alcohols . The present invention is based on the discovery of certain benefits of utilizing a Fischer-Tropsch synthesis catalyst comprising a combination of cobalt and manganese, at a particular weight ratio, in increasing the activity and selectivity of the Fischer-Tropsch reaction for the preparation of alcohols and liquid hydrocarbons.

U.S. Pat. No. 5,981,608 describes the use of a supported catalyst comprising cobalt and manganese, where the atomic ratio of cobalt to manganese in the catalyst is at least 12:1, for use in improving the C₅₊ hydrocarbon selectivity of a Fischer-Tropsch process. Similarly,

U.S. Pat. No. 5,958,985 describes the use of a catalyst comprising cobalt and manganese in a cobalt/manganese molar ratio of from 13:1 to 9:1 for improving the C₅₊ hydrocarbon selectivity of a Fischer-Tropsch process. However, neither of these documents describes how to modify the catalyst composition for improving activity and selectivity of a Fischer-Tropsch process for the production of alcohols and liquid hydrocarbons (below approximately C₂₄).

It has been surprisingly found that a supported catalyst comprising manganese and cobalt, present at a weight ratio of manganese to cobalt, on an elemental basis, of from 0.2 or greater, and comprising at least 2.5 wt. % of manganese, on an elemental basis, is particularly useful in improving activity and selectivity of a Fischer-Tropsch process for the production of alcohols and also olefins.

In a first aspect, the present invention provides a process for converting a mixture of hydrogen and carbon monoxide gases to a composition comprising alcohols and liquid hydrocarbons by means of a Fischer-Tropsch synthesis reaction, said process comprising contacting a mixture of hydrogen and carbon monoxide gases, preferably in the form of synthesis gas mixture, with a supported Co—Mn Fischer-Tropsch synthesis catalyst, wherein: the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zirconia, and ceria; the supported synthesis catalyst comprises at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; the weight ratio of manganese to cobalt, on an elemental basis, is 0.2 or greater; the molar ratio of hydrogen to carbon monoxide is at least 1; and, the Fischer-Tropsch synthesis reaction is conducted at a pressure in the range of from 1.0 to 10.0 MPa absolute.

In another aspect, the invention provides a supported Co-Mn Fischer-Tropsch synthesis catalyst comprising at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; and wherein the weight ratio of manganese to cobalt present, on an elemental basis, is 0.2 or greater, preferably 0.3 or greater, the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria, and wherein the supported Co—Mn Fischer-Tropsch synthesis is prepared by impregnation.

In a further aspect, the invention provides a supported Co—Mn Fischer-Tropsch synthesis catalyst comprising Co₃O₄ crystallites having a particle size of less than 100 Angstroms, and comprising at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; and wherein the weight ratio of manganese to cobalt, on an elemental basis, is 0.2 or greater, and the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria.

In yet a further aspect, the invention provides a process for preparing a supported Co—Mn Fischer Tropsch synthesis catalyst as defined herein, wherein the synthesis catalyst is obtained or obtainable from a process comprising the steps of:

(a) impregnating a support material with: a cobalt-containing compound and a manganese-containing compound in a single impregnation step to form an impregnated support material; and (b) drying and calcining the impregnated support material to form the supported Co—Mn Fischer-Tropsch synthesis catalyst.

Also provided are uses of a supported Co—Mn Fischer-Tropsch synthesis catalyst as defined herein for: i) increasing the selectivity of a Fischer-Tropsch process for the production of alcohols; and/or ii) increasing conversion in a Fischer-Tropsch process.

The present invention provides a process for converting a mixture of hydrogen and carbon monoxide gases to a composition comprising alcohols and liquid hydrocarbons by means of a Fischer-Tropsch synthesis reaction, said process comprising contacting a mixture of hydrogen and carbon monoxide gases, preferably in the form of synthesis gas mixture, with a supported Co—Mn Fischer-Tropsch synthesis catalyst. The product composition produced by the Fischer-Tropsch synthesis reaction will also comprise other components, such as waxes as well as other oxygenates, however, the process of the present invention exhibits an increase in selectivity to alcohols and liquid hydrocarbons compared to conventional Fischer-Tropsch synthesis reactions using a cobalt-based catalyst.

The term “liquid hydrocarbons” used herein in reference to the products of the Fischer-Tropsch reaction refers to C4 to C24 hydrocarbons. In some or all embodiments, the liquid hydrocarbons comprise at least 1 wt. % olefins, for example at least 2 wt. % olefins or at least 3wt. % olefins, such as at least 5 wt. % olefins, at least 10 wt. % olefins, or at least 20 wt. % olefins; preferably, the olefins will comprise linear alpha olefins, more preferably the olefins will comprise at least 50 wt. % linear alpha olefins, such as at least 70 wt. % linear alpha olefins.

The term “alcohols” used herein in reference to the products of the Fischer-Tropsch reaction refers to an alcohol having any number of carbon atoms. The alcohols are typically acyclic and may be straight- or branched-chain, preferably straight-chain. In some or all embodiments, the alcohols will comprise at least 50 wt. % linear alpha alcohols, such as at least 70 wt. % linear alpha alcohols or at least 80 wt. % linear alpha alcohols.

In some embodiments, the alcohols prepared by the process of the present invention include a major proportion (above 50 wt. %) of short-chain length C₁ to C₄ alcohols. In other embodiments, the alcohols prepared by the process of the present invention include a major proportion (above 50 wt. %) of medium-chain length C₅ to C₉ alcohols. In other embodiments, the alcohols prepared by the process of the present invention include a major proportion (above 50 wt. %) long-chain length C₁₀ to C₂₅ alcohols. The amount of alcohols produced by the Fischer-Tropsch reaction, and the relative proportion of short, medium and long chain may be determined by on-line GC mass spectrometry or other suitable technique.

In some or all embodiments, at least 15 wt. % of the products having a carbon chain length in the range of from C₈ to C₂₄ are alcohols. In some or all embodiments, at least 20 wt. % of the products having a carbon chain length in the range of from C₈ to C₂₄ are alcohols.

In some or all embodiments, the process of the present invention has a combined selectivity for alcohols and olefins of at least 15%, for example at least 20%, or even at least 40%. In some or all embodiments, the process of the present invention provides a product composition wherein in the C₈ to C₂₄ carbon chain length range, the combined selectivity for alcohols and olefins is at least 15%, for example at least 20%, or even at least 40%.

In some or all embodiments, the process of the present invention has a selectivity for alcohols of at least 15%, for example at least 20%, or even at least 40%. In some or all embodiments, the process of the present invention provides a product composition wherein in the C8 to C24 carbon chain length range, the selectivity for alcohols is at least 15%, for example at least 20%, or even at least 40%.

In some or all embodiments, the process of the present invention has a combined alcohol and olefin productivity of at least 50 g/L·h (grams per litre of catalyst per hour), for example at least 70 g/L·h, or even at least 90 g/L·h. In some or all embodiments, the process of the present invention provides a product composition wherein in the C8 to C24 carbon chain length range, the combined alcohol and olefin productivity is at least 50 g/L·h, for example at least 70 g/L·h, or even at least 90 g/L·h.

In some or all embodiments, the process of the present invention has an alcohol productivity of at least 50 g/L·h, for example at least 70 g/L·h, or even at least 90 g/L·h. In some or all embodiments, the process of the present invention provides a product composition wherein in the C8 to C24 carbon chain length range, the alcohol productivity is at least 50 g/L·h, for example at least 70 g/L·h, or even at least 90 g/L·h.

The combination of the total amount of manganese and the weight ratio of manganese to cobalt has been found to be important to the process of the present invention. In particular, the use of a catalyst having this combination of total amount of manganese and the weight ratio of manganese to cobalt in a Fischer-Tropsch synthesis as described, it have been found to produce a product composition having a significant proportion of alcohols, and, advantageously, for each carbon chain length having from 8 to 24 carbon atoms, at least 15%, for example at least 20%, of each carbon chain length is an alcohol. In some or all embodiments, at least 15 wt. % of the C₈ to C₂₄ carbon chain length molecules are alcohols, for example at least 20 wt. % or even at least 30 wt. % of the C₈ to C₂₄ carbon chain length molecules are alcohols.

Without wishing to be bound by theory, it is believed that preparing a catalyst which comprises at least 2.5 wt. % manganese and a manganese to cobalt weight ratio, on an elemental basis, of at least 0.2, by impregnation, the cobalt oxide crystallite (Co₃O₄) sizes in the resulting supported Co—Mn Fischer-Tropsch synthesis catalyst are of a particle size which may give rise to, or contribute to, benefits when the catalyst is utilized in a Fischer-Tropsch reaction. In particular, the cobalt oxide crystallite (Co₃O₄) particle sizes resulting from the combination of total amount of manganese and the weight ratio manganese to cobalt weight ratio employed in the present invention have been found to be less than 100 Angstroms (10 nm), for example less than 80 Angstroms (8 nm), preferably less than 60 Angstroms (6 nm), such as less than 40 Angstroms (4 nm) or less than 35 Angstroms (3.5 nm). This crystallite size is of the same order, and even notably smaller than the cobalt particle size indicated as being particularly preferred for optimal activity and selectivity for C₅₊ hydrocarbons in de Jong et al., discussed hereinbefore, namely 6 to 8 nm. Nevertheless, once the Co—Mn Fischer-Tropsch synthesis catalyst is activated and utilized in a Fischer-Tropsch reaction, productivity and selectivity for alcohols is notably enhanced over cobalt-containing synthesis catalysts comprising no manganese, or an insufficient amount of manganese having regard to the criteria of the present invention. Additionally, without being bound by theory, it is believed that the productivity and selectivity for olefins is notably enhanced over cobalt-containing synthesis catalysts comprising no manganese, or an insufficient amount of manganese having regard to the criteria of the present invention.

Without being bound by any particular theory, it is believed that the presence of manganese contributes to surface effects on the solid support which influences cobalt oxide crystallite development and dispersivity at the surface. This may derive from the mobility of cobalt-containing precursor compound(s) which are applied to the support material during catalyst preparation, for instance suspended or dissolved in an impregnation solution, whilst in the presence of manganese-containing precursor compound(s). Thus, the catalyst of the present invention preferably involves cobalt-containing precursor compound(s) and manganese-containing precursor compound(s) being applied to a support material such that they form a mobile admixture at the surface of the support during its preparation.

In some or all embodiments, the weight ratio of manganese to cobalt present in the supported Co—Mn Fischer-Tropsch synthesis catalyst, on an elemental basis, is from 0.2 to 3.0; specific examples of weight ratios of manganese to cobalt include from 0.2 to 2.0, from 0.2 to 1.5, from 0.2 to 1.0, from 0.2 to 0.8, from 0.3 to 2.0, from 0.3 to 1.5, from 0.3 to 1.0, and from 0.3 to 0.8. Typically, the weight ratio of manganese to cobalt present in the supported Co—Mn Fischer-Tropsch synthesis catalyst, on an elemental basis, is at least 0.3, more typically at least 0.3, and at most 1.5, more typically at most 1.0.

The benefits of the manganese loading and the weight ratio of elemental manganese to elemental cobalt according to the invention may be observed over a large range of concentrations of cobalt and manganese in the supported synthesis catalyst. However, in some or all embodiments, the supported synthesis catalyst comprises manganese, on an elemental basis, in an amount of at least 3.0 wt. % based on the total weight of the supported synthesis catalyst.

In preferred embodiments, the supported Co—Mn Fischer-Tropsch synthesis catalyst contains from 5 wt. % to 35 wt. % of cobalt, more preferably from 7.5 wt % to 25 wt % of cobalt, even more preferably from 10 to 20 wt. % of cobalt, on an elemental basis, based on the total weight of the supported synthesis catalyst.

In other preferred embodiments, the supported Co—Mn Fischer-Tropsch synthesis catalyst contains from 2.5 wt. % to 15 wt. % of manganese, preferably from 3.0 wt % to 12.5 wt % of manganese, for example from 3.0 to 10 wt. % of manganese, or even 4.0 to 8.0 wt. % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst.

The supported Co—Mn Fischer-Tropsch synthesis catalyst having a weight ratio of manganese to cobalt as described hereinbefore has been found to be particularly useful in Fischer-Tropsch reaction for providing selectivity for the production of alcohols, in particularly when the temperature of the Fischer-Tropsch reaction is in the range from 150 to 350° C., more preferably from 180 to 300° C., and most preferably from 200 to 260° C.

In the present invention, the Fischer-Tropsch synthesis reaction is conducted at a pressure in the range of from 10 to 100 bar (1.0 to 10.0 MPa) absolute. In preferred embodiments, the pressure of the Fischer-Tropsch reaction is in the range from 10 to 80 bar (from 1 to 8 MPa), more preferably from 10 to 60 bar (from 1 to 6 MPa), for example from 15 to 50 bar (from 1.5 to 5 MPa) or from 20 to 45 bar (from 2 to 4.5 MPa).

The supported Co—Mn Fischer-Tropsch synthesis catalyst used in accordance with the present invention may be prepared by any suitable method which is able to provide the required manganese to cobalt weight ratio and the required concentration of manganese on the supported. Preferably, the supported Co—Mn Fischer-Tropsch synthesis catalyst used in accordance with the present invention is prepared by a process in which the cobalt and the manganese are impregnated on to the support material.

A suitable impregnation method, for example, comprises impregnating a support material with cobalt-containing compound, which is thermally decomposable to the oxide form, and a manganese-containing compound. Impregnation of the support material with the cobalt-containing compound and the manganese-containing compound may be achieved by any suitable method of which the skilled person is aware, for instance by vacuum impregnation, incipient wetness or immersion in excess liquid.

The incipient wetness technique is so-called because it requires that the volume of impregnating solution be predetermined so as to provide the minimum volume of solution necessary to just wet the entire surface of the support, with no excess liquid. The excess solution technique as the name implies, requires an excess of the impregnating solution, the solvent being thereafter removed, usually by evaporation.

The support material may be in the form of a powder, granulate, shaped particle, such as a preformed sphere or microsphere, or extrudate. Reference herein to a powder or granulate of a support material is understood to refer to free flowing particles of a support material or particles of support material that have undergone granulation and/or sieving to be a particular shape (e.g. spherical) and size range. Reference herein to an “extrudate” is intended to mean a support material that has undergone an extrusion step and therefore may be shaped. In the context of the present invention, the powder or granulate is in a form which is suitable for impregnation with a solution of cobalt-containing compound and manganese-containing compound, and subsequent extrusion or forming into other shaped particles.

The support material used with the present invention comprises a material selected from titania, zinc oxide, alumina, zirconia, and ceria. Preferably, the support material is selected from the group consisting of ceria, zinc oxide, alumina, zirconia, titania, and mixtures thereof. More preferably, the support material is selected from titania and zinc oxide. Most preferably, the support material is selected from titania or mixtures containing titania. An example of a preferred titania support material particulate is titania powder, e.g. P25 Degussa.

It will be understood that the support material may be in any form provided it is suitable for use as a support for a Fischer-Tropsch synthesis catalyst and also preferably where the support material has not been previously impregnated with sources of metal other than cobalt and/or manganese which may have a deleterious effect on the performance of the active catalyst and may interfere with the benefits of the invention. Thus, whilst support material that has been previously loaded with cobalt and/or manganese metal, or precursors thereof, may be used in accordance with the invention, other pre-treatments providing sources of other metals are preferably to be avoided.

Preferred support materials are substantially free of extraneous components which might adversely affect the catalytic activity of the system. Thus, preferred support materials are at least 95% w/w pure, more preferably at least 98% w/w pure and most preferably at least 99% w/w pure. Impurities preferably amount to less than 1% w/w, more preferably less than 0.50% w/w and most preferably less than 0.25% w/w. The pore volume of the support is preferably more than 0.150 ml/g and preferably more than 0.30 ml/g. The average pore radius (prior to impregnation) of the support material is 10 to 500 Å, preferably 15 to 100 Å, more preferably 20 to 80 Å and most preferably 25 to 60 Å. The BET surface area is suitably from 2 to 1000 m²g, preferably from 10 to 600 m²/g, more preferably from 15 to 100 m²/g, and most preferably 30 to 60 m²/g.

The BET surface area, pore volume, pore size distribution and average pore radius may be determined from the nitrogen adsorption isotherm determined at 77K using a Micromeritics TRISTAR 3000 static volumetric adsorption analyser. A procedure which may be used is an application of British Standard methods BS4359:Part 1:1984 ‘Recommendations for gas adsorption (BET) methods’ and BS7591:Part 2:1992, ‘Porosity and pore size distribution of materials’—Method of evaluation by gas adsorption. The resulting data may be reduced using the BET method (over the pressure range 0.05-0.20 P/Po) and the Barrett, Joyner & Halenda (BJH) method (for pore diameters of 20-1000 Å) to yield the surface area and pore size distribution respectively.

Suitable references for the above data reduction methods are Brunauer, S, Emmett, P H, & Teller, E, J. Amer. Chem. Soc. 60, 309, (1938) and Barrett, E P, Joyner, L G & Halenda P P, J. Am Chem. Soc. , 1951 73 373-380.

When in the form of a powder, the median particle size diameter (d50) is preferably less than 50 μm, more preferably less than 25 μm. When the support material is in the form of a granulate, the median particle size diameter (d50) is preferably from 300 to 600 μm. Particle size diameter (d50) may suitably be determined by means of a particle size analyser (e.g. Microtrac S3500 Particle size analyser).

It is known to be beneficial to perform Fischer-Tropsch catalysis with a shaped particle, such as an extrudate, particularly in the case of fixed catalyst bed reactor systems. It is, for instance, known that, for a given shape of catalyst particles, a reduction in the size of the catalyst particles in a fixed bed gives rise to a corresponding increase in pressure drop through the bed. Thus, the relatively large shaped particles cause less of a pressure drop through the catalyst bed in the reactor compared to the corresponding powdered or granulated supported catalyst. Shaped particles, such as extrudates, also generally have greater strength and experience less attrition, which is of particular value in fixed bed arrangements where bulk crush strength must be very high.

Reference herein to “impregnation” or “impregnating” is intended to refer to contact of the support material with a solution, or solutions, of a cobalt-containing compound and a manganese-containing compound, before drying in order to achieve precipitation of the cobalt-containing compound and the manganese-containing compound. Impregnation with a fully dissolved solution, or solutions, of the cobalt-containing compound and the manganese-containing compound ensures good dispersion of the cobalt-containing compound and the manganese-containing compound on the support material and is thus preferred. This is in contrast, for instance, to the use of partially dissolved cobalt-containing compound and/or a partially dissolved manganese-containing compound in ‘solid solutions’ or suspensions, where the level of dispersion of the cobalt-containing compound and manganese-containing compound across the surface, and in the pores, of the support material can fluctuate depending on the nature of the precipitation on the support material. Furthermore, use of a fully dissolved solution, or solutions, of cobalt-containing compound and manganese-containing compound also has less of an impact upon the resulting morphology and bulk crush strength of an extrudate formed thereafter compared with solid solutions. Nevertheless, benefits of the present invention can also be realised in the case where a solid solution, or solutions, of a partially undissolved cobalt-containing compound and/or manganese-containing compound is used.

Where a powder or granulate of a support material is contacted with a solution, or solutions, of cobalt-containing compound and manganese-containing compound, the amount of solution used preferably corresponds to an amount of liquid which is suitable for achieving a mixture which is of a suitable consistency for further processing, for example for shaping by extrusion. In that case, complete removal of the solvent of the impregnating solution may be effected after formation of the shaped particle, such as an extrudate.

Suitable cobalt-containing compounds are those which are thermally decomposable to an oxide of cobalt following calcination and which are preferably completely soluble in the impregnating solution. Preferred cobalt-containing compounds are the nitrate, acetate or acetylacetonate of cobalt, most preferably the nitrate of cobalt, for example cobalt nitrate hexahydrate. It is preferred to avoid the use of the halides because these have been found to be detrimental.

Suitable manganese-containing compounds are those which are thermally decomposable following calcination and which are preferably completely soluble in the impregnating solution. Preferred manganese-containing compounds are the nitrate, acetate or acetylacetonate of manganese, most preferably the acetate of manganese.

The solvent of the impregnating solution(s) may be either an aqueous solvent or a non-aqueous, organic solvent. Suitable non-aqueous organic solvents include, for example, alcohols (e.g. methanol, ethanol and/or propanol), ketones (e.g. acetone), liquid paraffinic hydrocarbons and ethers. Alternatively, aqueous organic solvents, for example an aqueous alcoholic solvent, may be employed. Preferably, the solvent of the impregnating solution(s) is an aqueous solvent.

In preferred embodiments, the impregnation of the support material with a cobalt-containing compound and a manganese-containing compound occurs in a single step, without any intermediate drying or calcination steps to separate the loading of the different components. As the skilled person will appreciate, the cobalt-containing compound and manganese-containing compound may be applied to the support material successively or simultaneously in separate impregnation solutions or suspensions, or preferably an impregnation solution or suspension comprising both the cobalt-containing compound and the manganese-containing compound is used.

The concentration of the cobalt-containing compound and the manganese-containing compound, in the impregnating solution(s) is not particularly limited, although preferably the cobalt-containing compound and the manganese-containing compound are fully dissolved, as discussed hereinbefore. When a powder or granulate of support material is impregnated and immediately followed by an extrusion step, the amount of the impregnating solution(s) is preferably suitable for forming an extrudable paste.

In a preferred embodiment, the concentration of the impregnating solution is sufficient to afford a supported catalyst containing from 5 wt. % to 35 wt. % of cobalt, more preferably from 7.5 wt % to 25 wt % of cobalt, even more preferably from 10 to 20 wt. % of cobalt, on an elemental basis, based on the total weight of the supported synthesis catalyst.

In another preferred embodiment, the concentration of the impregnating solution is sufficient to afford a supported catalyst containing from 2.5 wt. % to 15 wt. % of manganese, preferably from 3.0 wt % to 12.5 wt % of manganese, for example from 3.0 to 10 wt. % of manganese, or even 4.0 to 8.0 wt. % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst, following drying and calcination.

A suitable concentration of cobalt-containing compound and/or manganese-containing compound is, for example, 0.1 to 15 moles/litre.

It will be appreciated that where the support material is in powder or granulate form, once impregnated with a cobalt containing compound and a manganese-containing compound, the impregnated support material may be extruded or formed into shaped particles at any suitable stage before or after drying and calcining.

Impregnation of the support material is usually followed by drying of the impregnating solution in order to effect precipitation of the cobalt-containing compound and the manganese-containing compound on to the support material and preferably also to remove bound solvent of the impregnating solution (e.g. water). Drying therefore does not, for instance, lead to full decomposition of the cobalt-containing compound or otherwise lead to a change in oxidation state of the cobalt-containing compound. As will be appreciated, in embodiments where an extrusion is performed, complete drying and removal of solvent (e.g. bound solvent) of the impregnating solution may occur after forming of a shaped particle, for example by extrusion. Drying is suitably conducted at temperatures from 50° C. to 150° C., preferably 75° C. to 125° C. Suitable drying times are, for example, from 5 minutes to 72 hours. Drying may suitably be conducted in a drying oven or in a box furnace, for example, under the flow of an inert gas at elevated temperature.

Where a shaped particle, such as an extrudate, is impregnated, it will be appreciated that the support may be contacted with the impregnating solution by any suitable means including, for instance, vacuum impregnation, incipient wetness or immersion in excess liquid, as mentioned hereinbefore. Where a powder or granulate of support material is impregnated, the powder or granulate may be admixed with the impregnating solution by any suitable means of which the skilled person is aware, such as by adding the powder or granulate to a container of the impregnating solution and stirring.

Where a step of forming a shaped particle, such as an extrusion step, immediately follows impregnation of a powder or granulate, the mixture of powder or granulate and impregnating solution may be further processed if it is not already in a form which is suitable for forming a shaped particle, for instance by extrusion. For instance, the mixture may be mulled to reduce the presence of larger particles that may not be readily extruded or otherwise formed into a shaped particle, or the presence of which would otherwise compromise the physical properties of the resulting shaped particle, for example an extrudate. Mulling typically involves forming a paste which is suitable for shaping, such as by extrusion. Any suitable mulling or kneading apparatus of which the skilled person is aware may be used for mulling in the context of the present invention. For example, a pestle and mortar may suitably be used in some applications or a Simpson muller may suitably be employed. Mulling is typically undertaken for a period of from 3 to 90 minutes, preferably for a period of 5 minutes to 30 minutes. Mulling may suitably be undertaken over a range of temperatures, including ambient temperatures. A preferred temperature range for mulling is from 15° C. to 50° C. Mulling may suitably be undertaken at ambient pressures. As stated hereinbefore, it will be appreciated that complete removal of bound solvent from the impregnation solution may be conducted to effect complete precipitation after forming of the shaped particle, such as by extrusion.

In embodiments where a calcination step is performed on an impregnated powder or granulate, thereby completely removing solvent of the impregnation solution, the calcined powder or granulate may also be further processed in order to form a mixture which is suitable for forming into shaped particles, for example by extruding. For instance, an extrudable paste may be formed by combining the calcined powder or granulate with a suitable solvent, for example a solvent used for impregnation, preferably an aqueous solvent, and mulled as described above.

Preparation of the supported Co—Mn Fischer-Tropsch synthesis catalyst involves a calcination step. As will be understood, calcination is required for converting the cobalt-containing compound which has been impregnated on the support material into an oxide of cobalt. Thus, calcination leads to thermal decomposition of the cobalt-containing compound, and not merely removal of bound solvent of an impregnating solution, as for instance in the case of drying.

Calcination may be performed by any method known to those of skill in the art, for instance in a fluidized bed or rotary kiln at a temperature of at least 250° C., preferably from 275° C. to 500° C. In some embodiments, calcination may be conducted as part of an integrated process where calcination and reductive activation of the synthesis catalyst to yield a reduced Fisher-Tropsch synthesis catalyst are performed in the same reactor.

In a particularly preferred embodiment, the supported Co—Mn Fischer-Tropsch synthesis catalyst used in the process of the invention is obtained or obtainable from a process comprising the steps of:

(a) impregnating a support material with: a cobalt-containing compound and a manganese-containing compound in a single impregnation step to form an impregnated support material; and

(b) drying and calcining the impregnated support material to form the supported Co—Mn Fischer-Tropsch synthesis catalyst.

A particular advantage of this embodiment is the expediency with which a support material may be modified and converted into a supported Co—Mn Fischer-Tropsch synthesis catalyst using only a single impregnation step followed by a drying and calcination step. Thus, in preferred embodiments, the support material used in connection with the invention has undergone no prior modification, for instance by the addition of promoters, dispersion aids, strength aids and/or binders, or precursors thereof, before impregnation in step (a) of the process.

The supported Co—Mn Fischer-Tropsch synthesis catalyst used in the process of the present invention may additionally comprise one or more promoters, dispersion aids or binders. Promoters may be added to promote reduction of an oxide of cobalt to cobalt metal, preferably at lower temperatures. Preferably, the one or more promoters is selected from the list consisting of ruthenium, palladium, platinum, rhodium, rhenium, chromium, nickel, iron, molybdenum, tungsten, zirconium, gallium, thorium, lanthanum, cerium and mixtures thereof. Promoter is typically used in a cobalt to promoter atomic ratio of up to 250:1 and more preferably up to 125:1, still more preferably up to 25:1, and most preferably 10:1. In preferred embodiments, the one or more promoters are present in the cobalt-containing Fischer-Tropsch synthesis catalyst obtained in an amount from 0.1 wt. % to 3 wt. %, on an elemental basis, based on the total weight of the supported synthesis catalyst.

The addition of the promoters, dispersion aids, strength aids, or binders may be integrated at several stages of the catalyst preparation process. Preferably, the promoters, dispersion aids or binders, or precursors thereof, is/are introduced during impregnation step(s) where the cobalt-containing compound and manganese-containing compound are introduced.

The supported Co—Mn Fischer-Tropsch synthesis catalyst may conveniently be converted into a reduced supported Co—Mn Fischer-Tropsch synthesis catalyst by reductive activation by any known means of which the skilled person is aware which is capable of converting cobalt oxide to the active cobalt metal. Thus, in one embodiment, the process of the invention further comprises a preceding step of reducing a Co—Mn Fischer-Tropsch synthesis catalyst to form a reduced Co—Mn Fischer-Tropsch synthesis catalyst by contacting with a hydrogen-containing gas stream. The step of forming a reduced synthesis catalyst may be carried out batch wise or continuously in a fixed bed, fluidised bed or slurry phase reactor, or in-situ in the same reactor as will be subsequently used for the Fischer-Tropsch synthesis reaction. Reduction is suitably performed at a temperature of from 150° C. to 500° C., preferably from 200° C. to 400° C., more preferably from 250° C. to 350° C.

As will be appreciated, the gaseous reactant mixture supplied to the Fischer-Tropsch reaction may also be suitable for reducing the supported Co—Mn Fischer-Tropsch synthesis catalyst to form a reduced supported Co—Mn Fischer-Tropsch synthesis catalyst in situ, without requiring any preceding or distinct reductive activation step.

In the Fischer-Tropsch reaction of the invention, the volume ratio of hydrogen to carbon monoxide (H₂:CO) in the gaseous reactant mixture is at least 1:1, preferably at least 1.1:1, more preferably at least 1.2:1, more preferably at least 1.3:1, more preferably at least 1.4:1, more preferably at least 1.5:1, or even at least 1.6:1. In some or all embodiments of the present invention, the volume ratio of hydrogen to carbon monoxide (H₂:CO) in the gaseous reactant mixture is at most 5:1, preferably at most 3:1, most preferably at most 2.2:1. Examples of suitable volume ratios of hydrogen to carbon monoxide (H₂:CO) in the gaseous reactant mixture include the ranges: from 1:1 to 5:1; from 1.1:1 to 3:1; from 1.2:1 to 3:1; from 1.3:1 to 2.2:1; from 1.4:1 to 5 : 1; from 1.4:1 to 3:1; from 1.4:1 to 2.2:1; from 1.5:1 to 3:1; from 1.5:1 to 2.2 : 1; and, from 1.6:1 to 2.2:1. The gaseous reactant stream may also comprise other gaseous components, such as nitrogen, carbon dioxide, water, methane and other saturated and/or unsaturated light hydrocarbons, each preferably being present at a concentration of less than 30% by volume.

As discussed hereinbefore, the Fischer-Tropsch synthesis process of the present invention has been surprisingly found to afford a Fischer-Tropsch catalyst exhibiting high selectivity for alcohols; the Fischer-Tropsch synthesis process of the present invention has also been surprisingly found to afford a Fischer-Tropsch catalyst exhibiting high selectivity for olefins. Furthermore, at least in some embodiments, the catalytic activity has also been found to be superior.

Conventional Fischer-Tropsch temperatures may be used in order to prepare alcohols and liquid hydrocarbons in accordance with the present invention. For example, the temperature of the reaction may suitable be in the range from 100 to 400° C., such as from 150 to 350° C., or from 150 to 250° C. The pressure of the reaction may suitably be in the range from 10 to 100 bar (from 1 to 10 MPa), such as from 15 to 75 bar (from 1.5 to 7.5 MPa), or from 20 to 50 bar (from 2.0 to 5.0 MPa). In preferred embodiments, the temperature of the Fischer-Tropsch reaction is in the range from 150 to 35° C., more preferably from 180 to 300° C., and most preferably from 200 to 260° C. In preferred embodiments, the pressure of the Fischer-Tropsch reaction is in the range from 10 to 100 bar (from 1 to 10 MPa), more preferably from 10 to 60 bar (from 1 to 6 MPa) and most preferably from 20 to 45 bar (from 2 to 4.5 MPa).

The Fischer-Tropsch synthesis reaction may be performed in any suitable type of reactor, for example it may be performed in a fixed bed reactor, a slurry bed reactor, or a CANs reactor.

In another aspect of the invention, there is provided a supported Co—Mn Fischer-Tropsch synthesis catalyst comprising at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; and wherein the weight ratio of manganese to cobalt present, on an elemental basis, is 0.2 or greater, the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria, and wherein the supported Co—Mn Fischer-Tropsch synthesis is prepared by impregnation.

In yet a further aspect of the invention, there is provided a supported Co—Mn Fischer-Tropsch synthesis catalyst comprising Co3O4 crystallites having a particle size of less than 100 Angstroms (10 nm), preferably less than 60 Angstroms (6 nm), and comprising at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; and wherein the weight ratio of manganese to cobalt, on an elemental basis, is 0.2 or greater, and the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria,.

In yet a further aspect of the invention, there is provided a supported Co—Mn Fischer Tropsch synthesis catalyst comprising at least 2.5 w % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; and wherein the weight ratio of manganese to cobalt present, on an elemental basis, is 0.2 or greater, the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria, and wherein the catalyst comprising Co₃O₄ crystallites having a particle size of less than 100 Angstroms (10 nm), preferably less than 60 Angstroms (6 nm).

Co₃O₄ crystallite particle sizes may be measured by any suitable means including chemisorption, microscopy or X-ray diffraction. Preferably, Co₃O₄ crystallite particle sizes are determined by X-ray diffraction.

As will be appreciated, the support material and methods for preparing the supported Co—Mn Fischer-Tropsch synthesis catalysts of the above further aspects of the invention may be as defined hereinbefore. For example, the synthesis catalysts are preferably obtained or obtainable from a process comprising the steps of:

(a) impregnating a support material with: a cobalt-containing compound and a manganese-containing compound in a single impregnation step to form an impregnated support material; and (b) drying and calcining the impregnated support material to form the supported Co—Mn Fischer-Tropsch synthesis catalyst.

The supported Co—Mn Fischer-Tropsch synthesis catalysts of the above further aspects of the invention may also be used for i) increasing the selectivity of a Fischer-Tropsch process for the production of alcohols; and/or ii) increasing conversion in a Fischer-Tropsch process.

In a still further aspect of the invention, there is provided a method for increasing the selectivity of a Fischer-Tropsch process for the production of alcohols, and/or increasing conversion in a Fischer-Tropsch process, said method comprising the step of supplying a supported Co—Mn Fischer-Tropsch synthesis catalyst as defined hereinbefore to a Fischer-Tropsch process.

In a yet further aspect of the invention, there is provided a method for controlling cobalt oxide crystallite size in the preparation of a supported cobalt-containing Fischer-Tropsch synthesis catalyst, said method comprising the step of supplying acetic acid, or a metal salt of acetic acid, during the impregnation of a support material with a cobalt-containing compound, wherein the metal is selected from the group consisting of ruthenium, palladium, platinum, rhodium, rhenium, manganese, chromium, nickel, iron, molybdenum, tungsten, zirconium, gallium, thorium, lanthanum, cerium and mixtures thereof; preferably wherein the metal is selected from manganese, ruthenium, rhenium and platinum, more preferably the metal is manganese.

The invention will now be further described by reference to the following Examples which are illustrative only. In the Examples, CO conversion is defined as moles of CO used/moles of CO fed×100 and carbon selectivity as moles of CO attributed to a particular product/moles of CO converted×100. Unless otherwise stated, temperatures referred to in the Examples are applied temperatures and not catalyst/bed temperatures. Unless otherwise stated, pressures referred to in the Examples are absolute pressures.

EXAMPLES Example 1—Catalyst Preparation

Co(NO₃)₂.6H₂O and Mn(OAc)₂.4H₂O were mixed in a solution with a small amount of water in varying amounts (see Table 1 below). This mixture was then added slowly to 100 g P25 TiO₂ powder and mixed to obtain a homogeneous mixture. The Co(NO₃)₂.6H₂O was used in an amount so as to give 10 wt. % elemental Co on TiO₂. The resultant paste/dough was extruded to form extrudate pellets and then dried and calcined at 300° C. Average size of Co3O4 crystallites on the TiO₂ support of each catalyst were determined using X-ray diffraction and verified by hydrogen chemisorption on the reduced catalyst and the results are also shown in Table 1 below.

TABLE 1 Mass of Mass of cobalt manganese Co₃O₄ nitrate Cobalt acetate Manganese crystallite hexahydrate loading tetrahydrate Loading Mn/Co size (g) (wt. %) (g) (wt. %) ratio (Å) 62 10 55 10 1 <30 60 10 40 7.5 0.75 <30 58 10 25 5 0.5 <30 57 10 16.2 3 0.30 34 56 10 10.8 2 0.20 49 56 10 7.6 1.5 0.15 57 56 10 5.4 1 0.10 81 55 10 0 0 — 107

The X-ray diffraction technique used to determine the Co₃O₄ crystallite size has a limit of detection of around 30 Angstroms, and as such crystallite size measurements of less than 30 Angstroms are reported as <30 Angstroms due to potentially significant margins of error in the measured crystallite sizes.

The results in Table 1 show a trend of reduction in the size of Co₃O₄ crystallites formed in the supported catalysts prepared in Example 1 as the Mn/Co ratio increases.

Example 2—General Procedure for Fischer-Tropsch Reactions

10 g of catalyst extruded pellets were loaded into a reactor and reduced under a H₂ stream (15 h, 300° C., 100% H₂, atmospheric pressure). The gaseous supply was switched to a mixture of hydrogen and carbon monoxide (H₂/CO=1.8) comprising 18% nitrogen and the pressure maintained at 4.3 MPa. The temperature was raised to achieve conversion and maintained throughout the Fischer-Tropsch reaction.

Example 3—Effect of Co/Mn Ratio on Selectivity in Fischer-Tropsch Reactions

The catalysts prepared in Example 1 were employed in Fischer-Tropsch synthesis reactions according to the general procedure of Example 2. CO conversion; alcohol and liquid hydrocarbons productivities; and CH₄ selectivity data were compiled and results for the above Examples are provided in Table 2 below. Exit gasses were sampled by on-line gas chromatography and analysed for alcohol, olefin, iso and normal parafins from their GC peaks. The productivity of the catalyst is defined as the weight in grams of products formed over the catalyst per litre of packed catalyst volume per hour of reaction time. Values for CO conversion, CH₄ selectivity, and productivity are average values obtained at steady state.

TABLE 2 Catalyst Mn/Co CO % % % liquid 10% Co+ ratio Conversion Alcohols Olefins hydrocarbons CH₄ Sel 0% Mn — 66 1 1.5 6.1 12.6 1% Mn 0.10 64 1 2.2 7.2 8.6 1.5% Mn 0.15 63 2 2.8 8.1 6.6 2% Mn 0.20 64 2.6 3.3 9.6 9.4 3% Mn 0.30 51 19.6 20.9 37.1 11.4

Table 3 below shows the alcohol selectivity by carbon number achieved for longer carbon chain lengths (i.e. the percentage of each carbon length that is present as an alcohol).

TABLE 3 Alcohol carbon 10% 10% Co, 10% Co, 10% Co, 10% Co, chain length Co 1% Mn 2% Mn 3% Mn 5% Mn C1 3.19% 5.39% 9.34% 12.95% 22.21% C2 0.00% 0.00% 0.00% 0.00% 0.00% C3 1.77% 2.25% 2.39% 4.25% 2.26% C4 1.34% 3.37% 7.52% 20.04% 8.63% C5 0.80% 2.92% 6.11% 17.57% 6.86% C6 0.89% 3.10% 6.40% 20.86% 9.16% C7 2.62% 4.95% 9.53% 24.99% 16.26% C8 3.29% 6.22% 10.49% 28.09% 21.76% C9 3.71% 6.96% 11.37% 29.88% 25.23% C10 4.41% 7.51% 11.98% 31.17% 28.97% C11 4.50% 7.58% 12.09% 31.49% 31.24% C12 4.28% 6.81% 11.69% 30.99% 33.25%

The results provided in Tables 2 and 3 is online data, and as a result does not include the alcohols contained in the wax product collection; offline analysis of the wax product collected showed a higher level of alcohol selectivity. The results in Table 2 and 3 demonstrate a dramatic increase in alcohol productivity as the Mn/Co ratio is increased from 0.20 to 0.30. These results are unexpected since the small Co₃O₄ crystallite size observed for the catalyst having a Mn/Co ratio of 0.3 used in accordance with the invention (34 Å) would be expected to be too far below the optimum of 8 nm reported in the literature in order for the productivity of any particular FT product to be favourable.

Further analysis of the alcohols produced in the above Fischer-Tropsch reactions also demonstrates the increase in alcohol production when the Mn/Co ratio is in accordance with the present invention applies to a wide range of carbon numbers, including long carbon chains of C₅-C₁₅ and higher.

Example 4—Catalyst Preparation

An amount of Co(NO₃)₂.6H₂O and an amount of Mn(OAc)₂.4H₂O were mixed in a solution with a small amount of water. This mixture was then added slowly to 100 g P25 TiO₂ powder and mixed to obtain a homogeneous mixture. Co(NO₃)₂.6H₂O was used in an amount so as to give approximately 10 wt. % elemental Co on TiO₂. The resultant paste/dough was extruded to form extrudate pellets and then dried and calcined at 300° C. Characterization was complete on the resulting catalysts using X-ray diffraction, H₂ chemisorption, elemental analysis, temperature programmed reduction and BET surface area techniques.

Several catalysts were made with between 55 and 62g of cobalt hydrate hexahydrate, and between 0 and 55g of manganese acetate tetrahydrate to give different manganese loadings and different Mn:Co ratios as detailed in Table 4.

TABLE 4 Mass of cobalt Cobalt Mass of manganese Manganese Mn/ nitrate hexahydrate loading acetate tetrahydrate Loading Co (g) (wt. %) (g) (wt. %) ratio 62 10 55 10 1.00 60 10 40 7.5 0.75 58 10 25 5 0.50 57 10 16.2 3 0.30 56 10 10.8 2 0.20 56 10 7.6 1.5 0.15 56 10 5.4 1 0.10 55 10 0 0 0.00

Example 5—General Procedure for Fischer-Tropsch Reactions

1 ml samples of catalyst in the form of a powder were loaded into a high throughput parallel reactor and reduced under a H₂ stream (15 h, at 300° C., 100% H₂, atmospheric pressure). The gaseous supply was switched to a mixture of hydrogen and carbon monoxide (H₂/CO=1.8) comprising 18% nitrogen and the pressure maintained at 4.3 MPa. The temperature was raised to achieve conversion of 55-65% and maintained throughout the Fischer-Tropsch reaction. On line analytics were completed by GC. A second series of catalyst test were performed in a similar manner, except that 1 ml samples of catalyst in the form of extrudates were used instead of powders, and the H₂/CO ratio was 1.5. The results are presented in Tables 5 and 6.

TABLE 5 CO Methane C5+ % OH % OH % OH Conversion/ Selectivity Selectivity/ fraction fraction fraction % % % of C8 of C10 of C12 0% Co 5% Mn 0.2 — — — — — 10% Co 62.6 4.1 89.9 5.7 6.2 4.2 (comparative) 10% Co/1% Mn 59.1 4.1 88.4 9.6 10.8 7.0 (comparative) 10% Co/3% Mn 55.5 6.6 68.1 31.7 44.7 27.3 10% Co/5% Mn 66.8 10.5 63.8 36.0 48.9 26.8 10% Co/7.5% Mn 57.6 9.9 64.5 36.0 50.6 30.7 10% Co/10% Mn 53.2 10.9 61.4 34.6 52.4 31.1 catalysts tested at 42barg, 1.8 H2:CO, 1500 hr⁻¹ GHSV, tested as powders (125-160 um), conversion levels between 53 and 66%.

TABLE 6 CO Methane C5+ % OH % OH % OH Conversion/ Selectivity Selectivity/ fraction fraction fraction % % % of C8 of C10 of C12 0% Co 5% Mn 0.0 — — — — — 10% Co 33.3 4.9 90.3 3.8 3.8 1.8 (comparative) 10% Co/1% Mn 32.0 3.5 89.1 7.8 8.6 6.2 (comparative) 10% Co/3% Mn 37.5 5.5 70.5 26.9 40.9 27.7 10% Co/5% Mn 35.1 10.9 60.2 32.6 54.4 35.0 10% Co/7.5% Mn 32.2 10.6 59.4 32.4 56.8 36.7 catalysts tested at 42barg, 1.5 H2:CO, 1500 hr-1 GHSV, tested as extrudates (1.25-3.5 mm), conversion levels between 32 and 37%

Analysis of the wax product was also performed and 2-dimensional GC analysis and is presented as FIG. 1. This clearly showed the high intensity response associated with the oxygenate material that is produced in the long chain wax product. The size of the C17OH response is similar or larger than the C20 alkane response.

Compositional analysis of waxes produced using the powder form catalyst for 0, 1, 3 and 5 wt. % Mn loadings are presented in Table 7.

TABLE 7 Total Average Total alcohol n-paraffin 10% Co/TiO2+ Carbon Number (% w/w) (% w/w) 0% Mn 28 4.6 91.4 (comparative) 1% Mn 28 10.2 89.8 (comparative) 3% Mn 25 37.4 62.6 5% Mn 27 44.2 55.6

Example 7—Higher Loading Catalysts Two catalysts having higher cobalt loadings 19 wt. % and 25 wt. % cobalt, with 4 wt. %

and 6 wt. % manganese respectively, were prepared in a similar way as those described in Example 5. The Co₃O₄ crystal size was measure using XRD as 87 Å (8.7 nm) for the 25% Co, 6% Mn/TiO₂ catalyst, and 88 Å (8.8nm) for the 19% Co/4% Mn/TiO₂.

These catalyst were tested using the method as described in Example 6 and the results are presented in Tables 8 and 9.

TABLE 8 CO Methane C5+ % OH % OH % OH Conversion/ Selectivity Selectivity/ fraction fraction fraction % % % of C8 of C10 of C12 19% Co/4% Mn 57.0 14.3 59.9 31.1 33.0 30.9 25% Co/6% Mn 64.5 17.5 56.5 34.1 38.5 35.1 catalysts tested at 42barg, 1.8 H2:CO, 1500 hr-1 GHSV, tested as powders (125-160 um), conversion levels between 53 and 66%.

TABLE 9 CO Methane C5+ % OH % OH % OH Conversion/ Selectivity Selectivity/ fraction fraction fraction % % % of C8 of C10 of C12 19% Co/4% Mn 31.5 14.9 57.4 33.3 32.7 33.8 25% Co/6% Mn 32.8 17.8 53.2 31.6 36.5 37.2 catalysts tested at 42barg, 1.5 H2:CO, 1500 hr-1 GHSV, tested as extrudates (1.25-3.5 mm), conversion levels between 32 and 37% 

1. A process for converting a mixture of hydrogen and carbon monoxide gases to a composition comprising alcohols and liquid hydrocarbons by means of a Fischer-Tropsch synthesis reaction, said process comprising contacting a mixture of hydrogen and carbon monoxide gases with a supported Co—Mn Fischer-Tropsch synthesis catalyst, wherein: the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria; the supported synthesis catalyst comprises at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; the weight ratio of manganese to cobalt, on an elemental basis, is 0.2 or greater; the molar ratio of hydrogen to carbon monoxide is at least 1; and the Fischer-Tropsch synthesis reaction is conducted at a pressure in the range of from 1.0 to 10.0 MPa absolute.
 2. A process according to claim 1, wherein the support material comprises titania.
 3. A process according to claim 2, wherein the support material is titania.
 4. A process according to claim 1, wherein the weight ratio of manganese to cobalt present in the supported Co—Mn Fischer-Tropsch synthesis catalyst, on an elemental basis, is in the range of from 0.2 to 3.0.
 5. A process according to claim 1, wherein the supported Co—Mn Fischer-Tropsch synthesis catalyst contains from 5 wt. % to 35 wt. % of cobalt, on an elemental basis, based on the total weight of the supported synthesis catalyst
 6. A process according to claim 1, wherein the supported Co—Mn Fischer-Tropsch synthesis catalyst contains from 2.5 wt. % to 15 wt. % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst.
 7. A process according to claim 1, wherein the combined amount of cobalt and manganese in the supported Co—Mn Fischer-Tropsch synthesis catalyst is less than 30 wt. %, on an elemental basis, based on the total weight of the supported synthesis catalyst.
 8. A process according to claim 1, wherein the synthesis catalyst comprises Co₃O₄ crystallites having a particle size of less than 100 Angstroms.
 9. A process according to claim 1, wherein the Fischer-Tropsch synthesis reaction is conducted at a temperature of less than or equal to 300° C.
 10. A process according to claim 1, wherein the Fischer-Tropsch synthesis reaction is conducted at a pressure of less than 7.5 MPa absolute.
 11. A process according to claim 1, wherein the alcohols are C₅₊ alcohols.
 12. A supported Co—Mn Fischer-Tropsch synthesis catalyst comprising at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; and wherein the weight ratio of manganese to cobalt present, on an elemental basis, is 0.3 or greater, the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria, and wherein the supported Co—Mn Fischer-Tropsch synthesis is prepared by impregnation.
 13. A supported Co—Mn Fischer-Tropsch synthesis catalyst comprising Co₃O₄ crystallites having a particle size of less than 100 Angstroms and comprising at least 2.5 wt % of manganese, on an elemental basis, based on the total weight of the supported synthesis catalyst; and wherein the weight ratio of manganese to cobalt, on an elemental basis, is 0.2 or greater, and the support material of the supported Co—Mn Fischer-Tropsch synthesis catalyst comprises a material selected from titania, zinc oxide, zirconia, and ceria.
 14. A process for preparing a supported Co—Mn Fischer Tropsch synthesis catalyst as defined in claim 12 the process comprising the steps of: (a) impregnating a support material with: a cobalt-containing compound and a manganese-containing compound in a single impregnation step to form an impregnated support material; and (b) drying and calcining the impregnated support material to form the supported Co—Mn Fischer-Tropsch synthesis catalyst.
 15. A process according to claim 14, wherein the support material is impregnated with a solution or suspension comprising both the cobalt-containing compound and the manganese-containing compound.
 16. A process according to claim 14, further comprising a step of reducing the supported Co—Mn Fischer-Tropsch synthesis catalyst to form a reduced supported Co—Mn Fischer-Tropsch synthesis catalyst by contacting with a hydrogen-containing gas stream.
 17. A process according to claim 16, wherein reduction is performed at a temperature of from 200° C. to 400° C.
 18. A process for converting a mixture of hydrogen and carbon monoxide gases to a composition comprising alcohols and liquid hydrocarbons by means of a Fischer-Tropsch synthesis reaction, the process comprising contacting a mixture of hydrogen and carbon monoxide gases with a supported Co—Mn Fischer-Tropsch synthesis catalyst as defined in claim
 12. 19. A process according to claim 1, wherein the mixture of hydrogen and carbon monoxide gases is in the form of synthesis gas mixture.
 20. A process for preparing a supported Co—Mn Fischer Tropsch synthesis catalyst as defined in claim 13, the process comprising the steps of: (a) impregnating a support material with: a cobalt-containing compound and a manganese-containing compound in a single impregnation step to form an impregnated support material; and (b) drying and calcining the impregnated support material to form the supported Co—Mn Fischer-Tropsch synthesis catalyst.
 21. A process for converting a mixture of hydrogen and carbon monoxide gases to a composition comprising alcohols and liquid hydrocarbons by means of a Fischer-Tropsch synthesis reaction, the process comprising contacting a mixture of hydrogen and carbon monoxide gases with a supported Co—Mn Fischer-Tropsch synthesis catalyst as defined in Claim
 13. 